Functions and Uses：
1. NG-66E can produce deposit with the eye-catching luster appearance and the superior leveling. Excellent ductility and low cost.
2. The produced bright nickel deposit has a very good affinity for the chrome plating and can be used in the multi-layer nickel plating process of the polished steel.
3. At a certain thickness of the multi-nickel system that having chromium as the final deposit, NG-66E received the excellent result in the CASS (copper accelerated acid salt spray test) corrosion test.
4. This process does not contain any chemicals that destroy the ozone layer.
Operating Components：
Nickel sulfate 225 ~ 357g / L
Nickel chloride 45 ~ 135g / L
Boric acid 41 ~ 50g / L
NG-610 brightener 6 ~ 15mL / L
SR-62 wetting agent 1 ~ 5mL / L
NR-63 softener 10 ~ 25mL / L
NG-66E brightener 1 ~ 4mL / L
PH 3.5-4.5
Temperature 57 ~ 68 ℃
Current density 2.2 ~ 10.8 A / dm2
1. NG-66E can produce deposit with the eye-catching luster appearance and the superior leveling. Excellent ductility and low cost.
2. The produced bright nickel deposit has a very good affinity for the chrome plating and can be used in the multi-layer nickel plating process of the polished steel.
3. At a certain thickness of the multi-nickel system that having chromium as the final deposit, NG-66E received the excellent result in the CASS (copper accelerated acid salt spray test) corrosion test.
4. This process does not contain any chemicals that destroy the ozone layer.
Operating Components：
Nickel sulfate 225 ~ 357g / L
Nickel chloride 45 ~ 135g / L
Boric acid 41 ~ 50g / L
NG-610 brightener 6 ~ 15mL / L
SR-62 wetting agent 1 ~ 5mL / L
NR-63 softener 10 ~ 25mL / L
NG-66E brightener 1 ~ 4mL / L
PH 3.5-4.5
Temperature 57 ~ 68 ℃
Current density 2.2 ~ 10.8 A / dm2