Functions and Uses：
1. The deposit can obtain superior gloss in the different ranges of current densities.
2. The gloss can reach the same level as the acidic zinc plating.
3. Adding system is simple and easy to operate.
4. No special activation required. Immediately using after the bath made up can assure the consistent result.
5. The deposit obtains low inner stress and excellent ductility.
6. Excellent adhesion and no blistering.
7. Outstanding corrosion resistance.
8. Fast deposition speed with superior coverage and leveling.
9. To improve the production efficiency.
Operating Components：
Zinc Metal 8~16g/L
Sodium hydroxide 110~150 g/L
NCZ-46A make up agent 8~12 mL/L
NCZ-46 B Brighten agent 0.5~1mL/L
NCZ-46C Purifying agent 1~3mL/L
Temperature 20~45℃
1. The deposit can obtain superior gloss in the different ranges of current densities.
2. The gloss can reach the same level as the acidic zinc plating.
3. Adding system is simple and easy to operate.
4. No special activation required. Immediately using after the bath made up can assure the consistent result.
5. The deposit obtains low inner stress and excellent ductility.
6. Excellent adhesion and no blistering.
7. Outstanding corrosion resistance.
8. Fast deposition speed with superior coverage and leveling.
9. To improve the production efficiency.
Operating Components：
Zinc Metal 8~16g/L
Sodium hydroxide 110~150 g/L
NCZ-46A make up agent 8~12 mL/L
NCZ-46 B Brighten agent 0.5~1mL/L
NCZ-46C Purifying agent 1~3mL/L
Temperature 20~45℃