Functions and Uses：
1. TL can produce the semi-bright nickel deposit of columnar structure that free of sulfur and with excellent extension and leveling force.
2. The deposit is suitable for the initial coating of multi-layer nickel system or nickel-chromium electrodeposits. At a certain thickness, the corrosion resistance of the produced deposit of double-nickel-composite got a very good result in the "Coated Chamber corrosion resistance test" and "CASS test".
3. High stability of solution and easy to manage. High impurity tolerance.
Operating Components：
Nickel ion 50 ~ 120g / L1. TL can produce the semi-bright nickel deposit of columnar structure that free of sulfur and with excellent extension and leveling force.
2. The deposit is suitable for the initial coating of multi-layer nickel system or nickel-chromium electrodeposits. At a certain thickness, the corrosion resistance of the produced deposit of double-nickel-composite got a very good result in the "Coated Chamber corrosion resistance test" and "CASS test".
3. High stability of solution and easy to manage. High impurity tolerance.
Operating Components：
Nickel chloride 10 ~ 60g / L
Boric acid 48 ~ 52g / L
TL-01 make up 9 ~ 12 mL / L
ATL-03 leveling agent 0.5 ~1.2mL / L
DA-25 Adjustment agent 0.2~0.5mL/L
SR-62 Wetting Agent 1.0~2.0 mL/L
PH 3.8 to 4.2
Temperature 52 ~ 59 ℃
Anodic current density 0.2 ~ 10 A/dm2
Cathode current density 0.5 ~ 30 A/dm2